Synthesis and characterization of Ce³⁺ doped silica (SiO₂) ) nanophosphors co-doped with Al³⁺ or Mg²⁺ ions

Simple item page
dc.contributor.advisorDejene, B. F.
dc.contributor.advisorSwart, H. C.
dc.contributor.authorKoao, Lehlohonolo Fortune
dc.date.accessioned2015-10-29T07:32:21Z
dc.date.available2015-10-29T07:32:21Z
dc.date.copyright2009-11
dc.date.issued2009-11
dc.date.submitted2009-11
dc.description.abstractIn recent studies, amorphous silica (SiO2) has been used as a host matrix for rare-earth ions to prepare luminescent materials that can be used in various light emitting devices. Sol-gel glasses have the potential to hold up to ≥10% dopants without losing their amorphous structure. However, before rare earth (RE) - doped sol-gel glasses can be used as luminescent material, several fluorescence quenching mechanisms must be overcome. There are several quenching mechanisms which are present in all materials that are more serious in sol-gel glasses. The first is cross relaxation which involves energy transfer between RE elements; the others are energy transfer through lattice vibrations and to hydroxyl (OH) groups which are present due to the use of water as the solvent during the preparation process. A few studies have demonstrated that the luminescence intensity of rare-earth doped silica can be improved through incorporation of co-dopants such as Al, TiO2, B and by annealing at high temperatures (e.g. > 500ºC). Following their footsteps and in order to make comparisons, we used aluminum as the codopant in some samples to investigate the effects on luminescence yield for various RE concentrations. We also investigated the effects of magnesium co-dopant and high temperature annealing on the luminescence intensity of rare-earth doped silica. In this work, the highest emission intensity was observed for the sample with a composition of 0.5 mol% Ce3+. Cerium doped silica glasses had broad blue emission corresponding to the D3/2- FJ transition at 445 nm but exhibited apparent concentration quenching after higher concentrations of 0.5 mol% Ce3+. Silica containing Mg2+ or Al3+ ions displayed an increase in luminescence intensity as the Mg2+ or Al3+ to Ce3+ ratio increases for the range investigated but significant luminescence enhancement was observed for Mg2+:Ce ratio greater than 20, while that of Al3+ co-doping had the highest luminescent intensity when the ratio of Al:Ce is 10:1. This enhanced photoluminescence was assigned to an energy transfer from the Mg nanoparticles, to result in enhanced emission from Ce3+. The Al3+ or Mg2+ ions disperses the Ce3+ clusters, enhancing 2F5/2 and 2F7/2 emissions due to increased ion-ion distances and decreased cross-relation.en_ZA
dc.identifier.urihttp://hdl.handle.net/11660/1482
dc.language.isoenen_ZA
dc.publisherUniversity of the Free State (Qwaqwa Campus)en_ZA
dc.rights.holderUniversity of the Free State (Qwaqwa Campus)en_ZA
dc.subjectNanoparticlesen_ZA
dc.subjectGelationen_ZA
dc.subjectSilica gelen_ZA
dc.subjectSilicaen_ZA
dc.subjectLuminescenceen_ZA
dc.subjectDissertation (M.Sc. (Physics))--University of the Free State (Qwaqwa Campus), 2009en_ZA
dc.titleSynthesis and characterization of Ce³⁺ doped silica (SiO₂) ) nanophosphors co-doped with Al³⁺ or Mg²⁺ ionsen_ZA
dc.typeDissertationen_ZA
Files
Original bundle
Now showing 1 - 1 of 1
Thumbnail Image
Name:
KoaoLF.pdf
Size:
2.14 MB
Format:
Adobe Portable Document Format
Description:
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed upon to submission
Description:
Download
Collections
All Electronic Theses and Dissertations
Masters Degrees (Physics)