Preparation and characterization of ethylene vinyl acetate copolymer/poly(lactic acid)/sugarcane bagasse composites for water purification
Loading...
Date
2016-01
Authors
Makhetha, Thollwana Andretta
Journal Title
Journal ISSN
Volume Title
Publisher
University of the Free State (Qwaqwa Campus)
Abstract
Excessive release of heavy metals into the environment due to industrialization and urbanization
has posed a great problem to the world. Heavy metal ions do not degrade, therefore they can give
bad effect to human body and the environment itself. The purpose of this study was to prepare
polymer/natural fibre composites to be used in water purification, specifically to remove lead ions
from contaminated water. PLA/EVA blends and PLA/EV A/SCB composites were successfully
prepared by melt mixing. The lower viscosity of PLA, the lower interfacial tension between PLA
and SCB, and the wetting coefficient of PLA/SCB being larger than I, all suggested that SCB
would preferably be in contact with PLA, despite PLA's relatively high crystallinity. A fairly good
dispersion of SCB in the PLA matrix was observed. PLA and EV A were also completely
immiscible, with the 50/50 w/w PLA/EV A sample showing a co-continuous morphology and the
70/30 w/w sample showing EV A dispersed as small spheres in the continuous PLA phase.
Exposed fibre ends were observed in the composites in some SEM pictures which were believed
to add to the efficiency of metal adsorption. The two polymers in the blend seemed to have
protected the SCB from thermal degradation, because the mass loss of SCB degradation
products was only observed at higher temperatures when incorporated in the blends. Although
this behaviour may imply that the prepared composites can be used at temperatures above 200
°C, which is the degradation temperature of pure SCB, it is also possible that the release of the
volati le SCB degradation products was delayed as a result of interaction with one or both
polymers. The impact properties depended more on the PLA:EV A ratio than on the presence
of SCB. The PLA/EV A blends showed two melting peaks at approximately the same
temperatures as those of the neat polymers, which confirms the complete immiscibility of PLA
and EV A at all investigated compositions.
It was further observed that the water absorption increased with an increase in SCB loading in
the composites. The main parameters that influenced lead ion sorption on SCB and
PLA/EV A/SCB composites were the initial concentration, contact time, and the pH value. It
was observed that more lead was adsorbed than one would expect if the partial coverage of the
fibre by the polymer is taken into account, and therefore it may be assumed that some of the
lead was trapped inside the cavities in the composites and that the polymers may also have
played a role in the metal complexation process, since both polymers have functional groups
that could interact with the lead ions. The metal impurities underwent monolayer adsorption.
Description
Keywords
Water -- Pollutiion, Heavy metals -- Environmental aspects, Bagasse, Water -- Purification -- Lead removal, Dissertation (M.Sc. (Chemistry))--University of the Free State (Qwaqwa Campus), 2016